Home > News > Daily News > The cause of die failure in stamping process
News
Daily News
Industry News
Company news
Certifications
Latest News

Gifts of love in ancient China

Jade pendants The ancient Chinese usually gave their lovers something small so that they could easily take it everywhere. A jade pendant is a good cho...

what is mild steel

Mild steel is a type of carbon steel with a low amount of carbon – it is actually also known as “low carbon steel.” Although ranges vary depending ...

10 Differences between a Businessman and Entrepreneur

10 Differences between a Businessman and Entrepreneur Business people and entrepreneurs have many similarities.However, they are not the same kind of ...

What is ALOCROM 1200 surface treatment

What is ALOCROM 1200surface treatment Alocrom 1200 is a rapidnon-electrolytic dip process which gives excellent protection against corrosionto both pa...

What is Kydex material

What is Kydexmaterial Kydex is a line of thermoplasticacrylic-polyvinyl chloride materials manufactured by Sekisui SPI. It has a widevariety of applic...

What is Over mold?

Overmolding is also called 2 times injection molding in China. Compared with the third-party material bonding, overmolding process makes the process f...

What is Alodine 5200 surface treatment

What is Alodine 5200surface treatment Alodine 5200 treatment is a chromiumfree product and specifically formulated for treating aluminium and its allo...

What is Black Oxide?

Black Oxide, blackening, oxidizing, oxiding, black passivating, gun bluing . . . these terms all refer to the process of forming a black iron oxide on...

How and When to Add Bend Reliefs to Sheet Metal Parts

What is a Bend Relief? A bend relief is nothing more than two small incisions cut into a piece of sheet metal to free the metal between the two. It se...

Privacy Policy

We will not collect and store your information in any form.
Contact Us
Vice General Manager: Ivy
Tel:86-13312953695
Tel:86-755-82737317/82737469
Fax:86-755-82737710
E-mail: sales910@xy-global.com, sales.china@xy-global.com
Postal Code: 518129
Off Add: Room1702,17F,Building#4,Tianan Cloud Park,No.2018 Xuegang Rd.,Longgang District,Shenzhen.
Factory Add:Daling Industrial Area,Shaling,Fenggang Town,Dongguan City Contact Now

The cause of die failure in stamping process

The cause of die failure in stamping process

liuweiqiong liuweiqiong 2017-09-27 20:33:09
Stamping is one of the practical processes for producing large quantities of parts. Die failure is the most common problem in stamping production, often resulting in shutdown, affecting the product cycle. Therefore, it is necessary to find the cause of mold failure as soon as possible and make reasonable maintenance.


1 die damage
Die damage refers to the mold cracking, breaking, rising and so on, dealing with mold damage problems, it must be from the mold design, manufacturing processes and the use of mold to find reasons.

2 clamping die
The main reasons causing mould clamping are: the die guide is incorrect and inclined. Otherwise, the fault will be enlarged and the die will be damaged.

3 die damage and maintenance
When the die repair technology is too complex and the cost of mould repair is too large and difficult, the maintenance cycle will be too long, and the normal production of stamping will be seriously affected. Generally speaking.


Timely maintenance of the mold to prevent damage to the mold can greatly reduce the cost of stamping mold production. When the pivot parts of the die are severely damaged, sometimes the convex and concave dies are damaged at the same time.

Under normal circumstances, the main failure mode of stamping is excessive wear. Deliver from new mold manufacturing. Until the burrs of the stamping parts exceed the standard, the parts size and the shape and position accuracy are too bad, and the mold can not be repaired or not repaired at all, the die can only be scrapped. From the new mold into use until the failure of scrap.